Common Surface Defects of Welded Steel Pipe

　　Common surface defects of welded steel pipe:

　　(1) layered steel

　　Layered wall steel tube means the cross section is divided into two floors, exposed steel surface showing the hierarchical vertical cracks. Some exhibits inside and outside surfaces of steel recessed or raised locally, layered rendering suddenly raised, dents or warping in and out of the weld.

　　(2) sticky scar

　　Pipe sticky scar refers to internal and external surfaces of the massive steel focal adhesion plaques scar.

　　(3) holes

　　Pipe through the hole refers to a local steel tube bi holes exist.

　　(4) open welding

　　Welded steel pipe opening means through long cracks in steel welds or partial showing of.

　　(5) Local lap welding

　　Welded steel pipe refers to a partial outer surface of the steel pipe presents a partial arc weld.

　　(6) Welding ditch

　　Pipe welding groove is the outer surface of the steel pipe occurs through a long groove weld.

　　(7) the collapse of welding

　　Welded steel pipe collapse refers to the outer surface of the weld metal skeletons showing through a long trench, where the surface of the corresponding convex edges.

　　(8) pipe joints dislocation

　　Steel tube joint dislocation refers to the steel pipe weld, occurred the phenomenon of staggered up and down.

评论

发表评论

此博客中的热门博文

The difference between high-quality seamless steel tubes and inferior seamless steel tubes

　　In daily steel procurement, the most irritating and irritating thing is the purchase of inferior seamless steel tubes, which affects product quality. How to identify inferior seamless steel pipe? Here we identify through the following methods: 　　1, poor quality seamless steel pipe surface is prone to scarring. 　　Mainly due to two reasons: 　　(1) There are many impurities in the inferior seamless steel tubes and the materials are not uniform. 　　(2) Inadequate guide equipment for poor quality pipe manufacturers is particularly prone to sticking steel. Contaminated pipes tend to produce scars when they bite into the roll. 　　2, poor quality seamless steel pipe is prone to tube folding. 　　The so-called folding is a variety of fold lines formed on the surface of the seamless steel pipe, and this defect often runs through the entire product. The reason for the folding is that the manufacturer is pursuing high efficiency in order to increase the output. In the production process, ...
阅读全文

Repeated order from regular Singapore Customer–ERW Steel pipe

Project location：Indonesia Product：ERW steel pipe Standard and material：ASTM A53 GRB;EN10219 S355J2H Specifications：88.9*5.49*6000mm;273.1*12.5*11800mm;355.6*12.5*6000mm;406.4*12.5*6000mm Application：stock use Arrival time：2024.1.10 This order is for a customer in Singapore. After receiving goods of the first order, the customer gave great recognition to Xinyue’s comprehensive services and product quality. We signed a second contract soon. The delivery date required by the customer for this order was very urgent. Xinyue formulated a plan and mobilized rescources immediately. We finally delivered the product on time while ensuring that the product met specifications and quality requirements. Xinyue is committed to establishing long-term partnerships with customers. We provide customers with personalized solutions and professional technical support to meet the needs of different projects and markets. We adhere to customer satisfaction as the center and continuously improv...
阅读全文

GCr15 tube heat treatment process parameters

　　GCr15 Pipe is a high carbon chromium bearing steel with less alloy content, good performance and wide application. After quenching and tempering, it has high and uniform hardness, good wear resistance and high contact fatigue performance. The cold working of the steel is medium in plasticity, the cutting performance is general, the welding performance is poor, the sensitivity to white spots is large, and the temper brittleness is obtained. 　　Chemical composition / element content (%) 　　C: 0.95-1.05 Mn: 0.20-0.40 Si: 0.15-0.35 S: <=0.020 P: <=0.027 Cr: 1.30-1.65 　　The heat treatment system is: steel bar annealing, annealing or oil quenching at 830-840 °C. 　　Heat treatment process parameters: 　　1. Ordinary annealing: heating at 790-810 °C, after the furnace is cooled to 650 °C, air cooling - HB170-207 　　2. Isothermal annealing: 790-810 ° C heating, 710-720 ° C isothermal, air cooling - HB207-229 　　3. Normal fire: 900-920 ° C heating, air cooling - HB270-390 　　4. H...
阅读全文